MONOKRISTALI YAG I SRTIO3 I NJIHOVI SPEKTRI- MERENJE GAP-A
MONOCRYSTALS YAG AND SRTIO3 AND THEIR SPECTRA – GAP
MEASUREMENTS
Autor: FILIP RISTOSKI III razred Matematička gimnazija, Beograd
Mentor: ALEKSANDRA DIMIĆ, dipl. Fizičar Fizički fakultet , Beograd
REZIME
Na uzorcima monokristala YAG i SrTiO3 u radu su ispitivane optičke osobine i njihovi energetski
procepi u cilju da se odredi kojoj vrsti materijala pripadaju. Za merenje je primenjena UV‒Vis
spektrofotometrijska metoda. Na osnovu osobina, opisane su primene ispitanih monokristala.
Oba uzorka imaju propustljivost preko 50 % u vidljivom delu spektra s tim što StTiO3 ima vedu
maksimalnu propustljivost. Apsorpcioni maksimum na osnovu koga je određena boja
monokristala odgovara boji ispitivanih uzoraka. Na osnovu vrednosti energetskog procepa
SrTiO3 koji je na talasnoj dužini od 403 nm i iznosi 3.08 eV, može se zaključiti da on pripada
poluprovodnicima. Ispitivani uzorak Yag čiji je energetski procep na talasnoj dužini od 301nm i
iznosi 4.12 eV pripada dielektricima.
Ključne reči: Monokristali, UV‒Vis metoda, energetski procep,
SUMMARY
The analyses of the optical properties and energy gaps of the samples of monocrystals
YAG and SrTiO3 were carried out in order to determine what kind of material they belong to.
The UV-Vis spectrophotometric method was used in this research. In accordance with the
defined properties, the application of the analyzed monocrystals was described. Permeability
values of both samples is over 50 % in the visible part of the spectrum. However, SrTiO3
possesses higher maximum permeability. The color of monocrystal is based on the absorption
maximum. The absorption maximum matches the color of the analyzed samples. Based on the
energy gap of the sample SrTiO3, which is on the wavelength of 403 nm and amounts to 3.08
eV, it belongs to the group of semiconductors. The tested sample, whose energy gap is one the
wavelength of 301nm and 4.12 eV, belongs to dielectrics.
Key words: Monocristals, UV-Vis method, Energy gap